Product Details:
|
| Product Name: | Nickel- Copper Desulfurization Adsorbent | Appearance: | Appearance Gray And Black Extrudate |
|---|---|---|---|
| Particle Size/mm: | ∮4×4-15 | Copper Oxide ，%， ≥: | 30 |
| Nickel Oxide ，%， ≥: | 10.0 | Bulk Density, Kg/l: | 0.8-1.0 |
| Radial Crushing Strength, N/cm ≥: | 180 | Reduced Radial Crushing Strength, N/cm ≥: | 100 |
| Surface Area M2/g ≥: | 70 | ||
| High Light: | Nickel copper desulfurization catalyst,black extrudate desulfurization catalyst |
||
Nickel- copper desulfurization adsorbent for remove arsenic and chlorine
Nickel- copper desulfurization adsorbent carries nickel and copper as main active components ,with special alumina as carrier and dispersant. In normal condition, It is reduced state. We provide oxidized or reduced state according to customer’s requirement. In addition to the effective removal of sulfur compounds, Nickel- copper desulfurization adsorbent sulfur protective agents can remove arsenic and chlorine. With this catalyst, the sulfur, arsenic, chlorine and other impurities is considerably reduced 0.2ppm - 0.5ppm.
Characteristics:
1. The high depuration. under the process condition of 200℃,0.7-0.8Mpa ,6-8h-1,the sulfur content can be reduced to less than 0.2 ppm from 5 ppm. If the sulfur content of raw materials is100ppm, the sulfur content can be reduced to less than 0.5ppm.
2. HTSR-1 is not only removal of hydrogen sulfide and other inorganic sulfur, but also organic sulfur
3. The product can remove arsenic and chlorination.
4. Because of the high strength, hard powder, and easy operation. It is a kind of ideal protection agent of precious metal catalyst
Physical and chemical properties:
| Item | index |
| Appearance | gray and black extrudate |
| Particle size/mm | ∮4×4-15 |
| copper oxide ,%, ≥ | 30 |
| nickel oxide ,%, ≥ | 10.0 |
| Bulk density, kg/l | 0.8-1.0 |
| Radial Crushing Strength, N/cm ≥ | 180 |
| Reduced radial crushing Strength, N/cm ≥ | 100 |
| Surface area m2/g ≥ | 70 |
Reference operating conditions:
Process conditions |
Temperature,℃ | Pressure, Mpa | Space velocity,hr-1 | |
| 80-220( normal 80-200) | ambient -1.5(normal 0.7-0.8) | Gas:100-1000 | Liquid :0.5-10.0 | |
| normal liquid space velocity 5-8 | ||||
| H2S In raw material | 100ppm | ≤0.5ppm；Breakthrough sulfur capacity:≥8% | ||
| Arsenide in raw material | 100ppb | ≤1ppb | ||
| chloride in raw material | 10ppm | ≤0.5ppm | ||
Packing: 40kg net weight iron drums innerlining double-layer plastic bags.