Product Details:
|
| Product Name: | Hydrocracking Catalyst | Chemical Composition: | WO3-NiO-Al2O3 |
|---|---|---|---|
| Shape: | Trilobite | Dimension Mm: | Φ1.5～1.7×3～8 |
| Bulk Density Kg/l: | 0.83～0.93 | Specific Surface Area M2/g: | ≥250 |
| Highlight: | hydrotreating catalyst,solid phosphoric acid catalyst |
||
Hydrocracking catalyst with possessing strong N-resistant property
Catalyst JL-G-3 was researched and developed by FRIPP. It is a kind of hydrocracking catalyst possessing strong N-resistant property. Catalyst JL-G-3 adopts molecular sieve US-SSY and amorphous Si-Al as cracking components, and adopts W-Ni as hydrogenation components so that it possesses higher activity and higher selectivity of mid-distillate.
The most important characteristic of catalyst JL-G-3 is the better N-resistant property. It is able to contain the higher activity and stability under the condition of the content of nitrogen in refining oil lower than 20～50ppm. Even under the condition of the content of nitrogen in refining oil between 80～100ppm, it also can stably run and be used in regeneration. Catalyst JL-G-3 was first used in the hydrocracking device of Liaoyang Petrochemical Company in April 1998, and the running result of catalyst JL-G-3 in industrial application is fairly good.
(I),Characteristics of the catalyst
| chemical composition | WO3-NiO-Al2O3 |
| shape | trilobite |
| dimension mm | Φ1.5～1.7×3～8 |
| bulk density kg/l | 0.83～0.93 |
| specific surface area m2/g | ≥250 |
| crushing strength N/mm | ≥18 |
| pore volume ml/g | ≥0.28 |
| abrasion W% | ＜1.5 |
(II),Activity index
technology parameters |
pressure MPa |
temperature ℃ |
volume space velocity h-1 | hydrogen oil volume ratio |
| 14.7 | 370 | 1.0 | 1200:1 | |
| feedstock | Saudi Arabia light oil,Iran mixed oil | |||
| product | the yield of diesel 16.33%; cetane number 0.17 | |||