Product Details:
|
| Product Name: | HYDROTREATING CATALYST | Appearance: | Trilobe Extrudates |
|---|---|---|---|
| Particle Size,mm: | Ф1.5-2.5*2-10 | Crushing Strength,N/cm: | Min150 |
| Bulk Density, Kg/L: | 0.68-0.75 | Surface Area,m2/g: | Min200 |
| Pore Volume, ML/g: | 0.40 | MoO3,wt%: | 14.5-16.5 |
| CoO, Wt%: | 3.5-4.5 | ||
| Highlight: | biological catalyst,solid phosphoric acid catalyst |
||
HYDROTREATING CATALYST
HYDROTREATING CATALYST JL-H-04
Characteristics: The catalyst which has the advantage of high HDS, good compression resistance and abrasive resistance, low loading density, high space velocity and renewable use, takes modified alumina as carrier, with molybdenum and cobalt as the active components.
Application:It is mainly used for prehydrogenation of high sulphur reforming material and kerosene hydrogenation to produce aviation kerosene.
Physical-chemical properties
Characteristics: The catalyst which has the advantage of high HDS, good compression resistance and abrasive resistance, low loading density, high space velocity and renewable use, takes modified alumina as carrier, with molybdenum and cobalt as the active components.
Application:It is mainly used for prehydrogenation of high sulphur reforming material and kerosene hydrogenation to produce aviation kerosene.
Physical-chemical properties
| item | target | item | target |
| appearance | Trilobe extrudates | Surface area,m2/g | min200 |
| Particle size,mm | Ф1.5-2.5*2-10 | Pore volume, mL/g | 0.40 |
| Crushing strength,N/cm | min150 | MoO3,wt% | 14.5-16.5 |
| Bulk density, kg/L | 0.68-0.75 | CoO, wt% | 3.5-4.5 |
Activity index:
| Process parameters | Hydrogen partial pressure,Mpa | temperature℃ |
Space velocity hr-1 |
Hydrogen to oil ratio,V/V |
| 1.6 | 270 | 8.0 | 80 | |
| Raw oil | Iranian atmosphere distillation gasoline | |||
| Product oil | sulfur max 0.5ppm,Nitrogen max0.5ppm | |||
Packing: iron drums innerlining double-layer plastic bags.