Product Details:
|
| Color: | White Powder | BET: | 240-380m2/g |
|---|---|---|---|
| SIO2: | 0.06-2.0 | Na2O: | Max0.08 |
| Fe2O3: | 0.02 | Dry Basis: | Min70 |
| Cas No: | 1344-28-1 | ||
| High Light: | aluminium oxide powder,white aluminum oxide |
||
Pseudoboehmite is an aluminium compound with the chemical composition AlO(OH). It consists of finely crystalline boehmite. However, the water content is higher than in boehmite.
Pseudo-boehmite powder is odorless, tasteless, non-toxic, high purity in crystalline phase, strong in caking property.
Pseudo-boehmite is white powder with high purity, low pile, large pore volume, high specific surface and good compatibility. It can be easily decentralized and soluble in the acid and alkali solution. It can become highly active alumina after low-temperature roasting and dehydration.
Mainly used as raw materials for the production of catalyst carrier, activated alumina, also as molecular sieve, and as cement for aluminum silicate refractory fibre, for examples, as a cement of the catalyst for semi-synthetic rare earth cement of the catalyst for semi-synthetic rare earth Y molecular sieve cracking, catalyst in making ethylene by alcohol dehydration and EO.
| Item | Pole Volume | Specfic Surface | Dry
Basis |
SiO2 | Dispersion
index |
Na2O | Fe2O3 |
| M1/g | M2/g | % | % | % | % | % | |
| HYN_001 | 0.70-0.90 | 240-320 | 70±1 | <0.06 | <0.08 | <0.02 | |
| 0.90-1.10 | 280-340 | 70±1 | <0.06 | <0.08 | <0.02 | ||
| HYN_002 | 0.70-1.10 | 240-380 | 70±1 | 0.5-2.0 | <0.08 | <0.02 | |
| 0.70-1.10 | 280-400 | 70±1 | 2-4 | <0.08 | <0.02 | ||
| 0.80-1.20 | 220-400 | 70±1 | >4 | <0.08 | <0.02 | ||
| HYN_003 | 0.70-1.20 | 200-300 | 70±1 | <0.02 | <0.01 | <0.01 | |
| HYN_004 | 0.37-0.45 | 240-280 | >60 | <0.06 | >96 | <0.10 | <0.02 |
| 0.37-0.45 | 240-280 | >60 | <0.06 | >96 | <0.05 | <0.02 |