Product Details:
|
| Bulk Density G/cm3: | 0.55-0.65 | BETm2/g: | ≥ 150 |
|---|---|---|---|
| Pole Volum Cm3/g: | ≥ 0.50 | Crush Stength N/Grain: | ≥ 100 |
| Na2O%: | ≤ 0.10 | Al2O3%: | ≥ 94 |
| Water Adsorption%: | ≥ 70 | ||
| High Light: | catalytic cracking catalyst,fcc additives |
||
Alumina Carrier Columnar in petrochemical, hydrodesulfurization, low temperature shift catalyst carrier
Alumina Carrier Columnar (clover shape)
This series of products with false water alumina gel X- Rhoactivated alumina production fast removal method and continuouscarbonization method for the production of components, made ofadvanced molding technology, high specific surface area, goodstability of compressive strength, low abrasion, proper pore structure, low content of impurities, the characteristics of active component impregnation properties good etc.,
and according to user requirements, using different process conditions, catalyst carrierto adjust the production performance of materialized different crystal phases, different diameter, different content of impurities.Widely used in petrochemical, hydrodesulfurization, low temperature shift catalyst carrier.
The main product type and technical indicator:
|
rType
|
Component
|
Appearance
|
Size
mm |
Bulk Density
g/cm3 |
BETm2/g
|
Pole Volum
cm3/g |
Crush stength N/Grain
|
Na2O%
|
Al2O3%
|
Water adsorption%
|
|
HYZ-001
|
Al2O3• nH2O
|
Column
|
3 × (4-10)
|
0.55-0.65
|
≥ 150
|
≥ 0.50
|
≥ 100
|
≤ 0.10
|
≥ 94
|
≥ 70
|
|
HYZ-002
|
Al2O3• nH2O
|
clover
|
3 × (4-10)
|
0.55-0.65
|
≥ 150
|
≥ 0.50
|
≥ 100
|
≤ 0.10
|
≥ 94
|
≥ 70
|
|
HYZ-003
|
Al2O3• nH2O
|
Column
|
3 × (4-10)
|
0.5-0.6
|
≥ 220
|
≥ 0.60
|
≥ 90
|
≤ 0.10
|
≥ 94
|
≥ 70
|
|
HYZ-004
|
Al2O3• nH2O
|
clover
|
3 × (4-10)
|
0.5-0.6
|
≥ 220
|
≥ 0.60
|
≥ 90
|
≤ 0.10
|
≥ 94
|
≥ 70
|
|
HYZ-005
|
Silicon aluminum composite
|
Column
|
3 × (4-10)
|
0.5-0.6
|
≥ 180
|
≥ 0.50
|
≥ 100
|
≤ 0.10
|
≥ 84
|
≥ 65
|
|
HYZ-006
|
Silicon aluminum composite
|
Clover
|
3 × (4-10)
|
0.5-0.6
|
≥ 180
|
≥ 0.50
|
≥ 100
|
≤ 0.10
|
≥ 84
|
≥ 65
|
|
HYZ-007
|
Titaniumaluminum composite
|
Column
|
3 × (4-10)
|
0.55-0.65
|
≥ 150
|
≥ 0.45
|
≥ 90
|
≤ 0.15
|
≥ 84
|
≥ 72
|
|
HYZ-008
|
Titaniumaluminum composite
|
Column
|
3 × (4-10)
|
0.55-0.65
|
≥ 150
|
≥ 0.45
|
≥ 90
|
≤ 0.15
|
≥ 84
|
≥ 72
|
|
HYZ-009
|
Al2O3• nH2O
|
Column
|
3 × (4-10)
|
0.70-0.80
|
≥ 180
|
≥ 0.40
|
≥ 80
|
≤ 0.10
|
≥ 94
|
≥ 50
|
|
HYZ-010
|
Al2O3• nH2O
|
Sphere
|
Φ 3-4
|
≥ 0.68
|
≥ 170
|
≥ 0.45
|
≥ 70
|
≤ 0.20
|
≥ 94
|
≥ 65
|
|
HYZ-011
|
Al2O3• nH2O
|
Sphere
|
Φ 5-7
|
≥ 0.68
|
≥ 170
|
≥ 0.45
|
≥ 130
|
≤ 0.25
|
≥ 94
|
≥ 50
|
|
HYZ-012
|
Al2O3• nH2O
|
Sphere
|
Φ 4-6
|
0.55-0.60
|
≥ 250
|
≥ 0.45
|
≥ 60
|
0.10-1.00
|
≥ 94
|
≥ 60-70
|
|
HYZ-013
|
Al2O3• nH2O
|
Clover
|
3 × (4-10)
|
0.45-0.60
|
≥ 350
|
≥ 0.65
|
≥ 70
|
≤ 0.10
|
≥ 95
|
≥ 80
|
The content of *Na2O according to user needs
Contact Person: Mr. James.Li
Tel: 86-13706436189
Fax: 86-533-6076766