|Product Name:||Cyclohexylamine Catalyst||Appearance:||Black Extrudates|
|Particle Size ,mm:||Ф5 * 5-10||Chemical Compostion:||Cobalt Plus Carrier|
|Cobalt Oxide ,wt%:||Min30||Crushing Strength, N/cm:||Min60|
|Bulk Density, Kg/l:||1.0 To 1.1|
solid phosphoric acid catalyst
JL-M-04 is mainly used for hydrogenation of aniline to cyclohexylamine. it can hydrogenate 100% aniline to less than 100ppm.
Its outstanding characteristics are as follows:
A. prominent low temperature activity. when reaction temperature reach 160℃, it has very high catalytic activity.
B. very good activity stability. It is not necessary to increase reaction temperature in the course of operating entirely.
C. perfect selectivity. The selectivity of aniline to cyclohexylamine is more than 98%.
D. very long service life. The catalysts’ service life can reach 5 to 8 years.
E. its loading density is lower 10-15% than other same kind of catalyst. This can obviously decrease the expenditure for purchasing catalyst.
The catalyst has been successfully used in several industry units. its comprehensive performance is superior to the same kind of products.
Physical and chemical properties:
|Particle size ,mm||Ф5 * 5-10|
|Chemical compostion||cobalt plus carrier|
|cobalt oxide ,wt%||min30|
|Crushing strength, N/cm||min60|
|Bulk density, kg/l||1.0 to 1.1|
reference operating conditions:
|Space velocity,h-1||Hydrogen to aniline molecular ratio|
|Raw material||Aniline min 98.5%,water max 0.4%,no sulfur and sulfides.|
Conversion of aniline, min 97%;cyclohexane content , min90%
Packing: iron drums innerlining double-layer plastic bags.